REVIEW ARTICLE
Year : 2021  |  Volume : 18  |  Issue : 1  |  Page : 72

Effect of total-etch and self-etch adhesives on the bond strength of composite to glass-ionomer cement/resin-modified glass-ionomer cement in the sandwich technique – A systematic review


1 Department of Conservative Dentistry and Endodontics, Dr. D. Y. Patil Dental College, Dr. D. Y. Patil Vidyapeeth, Pune, Maharashtra, India
2 Department of Pediatric and Preventive Dentistry, Pacific Dental College, Udaipur, Rajasthan, India

Date of Submission10-Mar-2020
Date of Acceptance19-Apr-2021
Date of Web Publication25-Sep-2021

Correspondence Address:
Dr. Amarjot Kaur D. S. Manihani
Dr. D. Y. Patil Dental College and Hospital, Dr.D. Y. Patil Vidyapeeth, Sant Tukaram Nagar, Pune - 411 018, Maharashtra
India
Login to access the Email id

Source of Support: None, Conflict of Interest: None


DOI: 10.4103/1735-3327.326645

Rights and Permissions
  Abstract 


The success of the sandwich technique depends on the bond strength of composite to glass-ionomer cement (GIC)/resin-modified glass-ionomer cement (RMGIC). Currently used adhesives employ the total-etch and the self-etch techniques. The total-etch system is technique sensitive, whereas the self-etch system is popular for its ease of use. The aim of this systematic review is to compare the effect of total-etch and self-etch adhesives (SEAs) on the bond strength of composite to GIC/(RMGIC) in the sandwich technique. A literature search was conducted using electronic databases (PubMed, Web of Science, Ebscohost, and Scopus) limiting the year of publications from January 1, 2000, to September 30, 2018, to identify the relevant studies. All the cross-references of the selected studies were also screened. In vitro studies on extracted human teeth were selected. A total of 10 articles were included in this review. A conclusion was drawn that SEAs when used in the sandwich technique resulted in greater bond strength in comparison to total-etch adhesives. Moreover, increased bond strength was achieved when the primer was employed on unset GIC as compared to set GIC. Furthermore, the application of SEAs over uncured RMGIC (co-curing technique) resulted in better bond strengths as compared to their application over cured RMGIC.

Keywords: Bond strength, composite resins, dentin-bonding agents, glass-ionomer cements


How to cite this article:
Manihani AK, Mulay S, Beri L, Shetty R, Gulati S, Dalsania R. Effect of total-etch and self-etch adhesives on the bond strength of composite to glass-ionomer cement/resin-modified glass-ionomer cement in the sandwich technique – A systematic review. Dent Res J 2021;18:72

How to cite this URL:
Manihani AK, Mulay S, Beri L, Shetty R, Gulati S, Dalsania R. Effect of total-etch and self-etch adhesives on the bond strength of composite to glass-ionomer cement/resin-modified glass-ionomer cement in the sandwich technique – A systematic review. Dent Res J [serial online] 2021 [cited 2021 Dec 8];18:72. Available from: https://www.drjjournal.net/text.asp?2021/18/1/72/326645




  Introduction Top


Resin-based composites have become the most popular and commonly used tooth-colored dental materials today. With a continuous upgradation of material properties, it is envisaged that the gap between basic material science and clinical implementation would soon be bridged. Weak bond strength, especially in the gingival margin, is one of the prime concerns.[1] Hence, a material-like glass-ionomer cement (GIC) or resin-modified glass-ionomer cement (RMGIC) that has a low resistance to elastic deformation is applied under composite restorations. This is popularly known as the sandwich/laminate technique that gives increased bond strengths.[2]

GIC, known for its chemical adhesion to dentin[3] and continued fluoride release;[4],[5] depicts increased bond strength over time. This is because of an ion-exchange layer present at the interface of the tooth and cement.[6] Nevertheless, they are highly susceptible to moisture uptake due to the slow-setting reaction.

RMGIC contains hydroxyethyl methacrylate (HEMA) and can be light cured.[7] It exhibits improved mechanical properties[8] and better resistance to moisture contamination in comparison to conventional GIC, while the fluoride release remains the same.[9],[10]

Laminate restorations are popularly employed in restorative dentistry where a GIC is placed between the tooth and composite resin. Developed by McLean et al., in 1985, the adherent properties of glass-ionomers were utilized to seal cavities and reduce microleakage.[11] The advantage of the strong bond strengths of acid-etched enamel to composite resins and the sustained fluoride-releasing property of GICs/RMGICs make the combined use of these two materials a vital step in ensuring adequate clinical results.[12],[13]

However, due to a lack of chemical bonding between the two materials, they show a limited bond strength. This is due to their different setting mechanisms.[14]

Recent trends in bonding include two concepts: the total-etch and self-etch. The former comprises a separate etching step and is technique sensitive, whereas the self-etch system is comparatively simpler and less technique sensitive.[15]

Although there has been a comprehensive description of etching of enamel and dentin prior to the use of adhesives and cements in dentistry, the pretreatment of GIC surface remains unclear.[16],[17] McLean et al. advocated the acid etching of conventional GICs for its integration with the adhesive/composite resin. This bond can be compared to the one formed between acid-etched enamel and composite.[18],[19] However, its major drawback is its sensitivity to moisture and the gradual loss in the amount of GIC which is responsible for its disintegration post etching. Due to the infusion of water in its early setting stage, the weak calcium-polyacrylate chains disintegrate, thus degrade the physical properties of the cement.

On the other hand, self-etch adhesives (SEAs) comprise either one or two steps, with the incorporation of self-etching primers that make their use less complex. Etching and resin infiltration are concomitant. Research has demonstrated that these systems produce similar enamel and dentin bond-strengths in comparison to total-etch adhesives (TEAs).[12],[20] An additional advantage of self-etch bonding agents is that they can be applied over unset GIC. Elimination of the rinsing step prevents moisture contamination and drying of GIC.[21]

The success of the sandwich technique is determined by the bond strength of GIC to dentin and resin composite. Several studies have been conducted to evaluate the effects of TEAs and SEAs on the bond strength of the sandwich technique. Bonding agents of various brands and with different pH values have been used for varied different application periods. However, the clinical implications of different bonding agents are still a dilemma for many clinicians.

Hence, this systematic review aims to interpret conflicting research data and current information regarding the use of bonding agents in the sandwich technique so that a clearer understanding and in-depth knowledge enables the clinician to use these materials judiciously for a more predictable outcome.


  Materials and Methods Top


The review was conducted in accordance with the preferred reporting items for systematic reviews and meta-analyses statement. A PICO (Population, intervention, comparison and outcomes) question was formulated to obtain the relevant studies. The PICO question was What is the effect of total-etch and SEAs on the bond strength of composite to GIC/RMGIC in the sandwich technique?

Where, P: Freshly extracted human teeth, I: SEAs, C: TEAs, and O: Increase or Decrease in Bond Strength between Composite to GIC/RMGIC.

Electronic databases (PubMed, Web of Science, Ebscohost, and Scopus) were searched for literature using different search strategies for the aforementioned keywords and their combinations. All the cross-references of the selected studies were also screened. In vitro studies on extracted human teeth were selected. Finally, the review comprised ten articles. An exploratory search was conducted by two authors using the combination of the following medical subject heading terms – composite, GIC bond strength, sandwich technique, TEAs, and SEAs [Table 1].
Table 1: The primary and secondary keywords used in this systematic review

Click here to view


The inclusion criteria comprised articles in the English language published between January 1, 2000, and September 30, 2018. In vitro studies on extracted human teeth evaluating the effect of both TEAs and SEAs on the bond strength of the sandwich technique were included. Exclusion criteria comprised reviews, case reports, abstracts, letters to editors, editorials, and in vivo studies.

Study selection

In vitro comparative studies were selected where bond strength was evaluated between composite and GIC after using self-etch or TEAs. A total of 522 articles were identified through the database searching and one article was identified through other sources. After a thorough screening of 523 articles, 63 articles were shortlisted. Furthermore, these records were assessed for duplicates and 42 articles were removed. The abstracts of the remaining 21 articles were then screened and 6 articles were excluded. Full texts were obtained for the 15 articles and assessed for eligibility after which 5 articles were excluded. Finally, 10 articles were included in this systematic review [Figure 1].
Figure 1: Preferred reporting items for systematic reviews and meta-analysis diagram illustrating the study selection process.

Click here to view


Data collection process

Data extraction was done for one article using Microsoft Excel and further reviewed by an expert and culminated. This was followed by data extraction of all the articles for the following parameters – author and year of study, country where the study was conducted, sample size, brand of composite, brand of GIC, self-etch and TEA, outcome variable, methodology, mean bond strengths of the self-etch and TEAs, statistical tests used for data analysis, and conclusion. Only data that were relevant to this study were retained [Table 2].
Table 2: Characteristics of the studies included in this review

Click here to view



  Results and Discussion Top


Several efforts have been made to achieve increased bond strengths between composite and GIC in the laminate technique. We thereby discuss the effects that both total-etch and SEAs have on the bond strength of composite to GIC/RMGIC.

Conventional glass-ionomer cement and composite

Set versus unset glass-ionomer cement

Gopikrishna et al.[21] studied the shear bond strength (SBS) of composite resin to GIC employing a total-etch, two-step self-etch, and GIC-based bonding system. They also evaluated the effect of the last two bonding systems over set and unset GIC. According to their study, the self-etch bonding system applied over unset GIC yielded the highest bond strength followed by the GIC-based adhesive system over set GIC. According to them, the carboxylic monomers in the SEA may have bonded to calcium in the unset GIC. The total-etch group and the group in which self-etch bonding agent was applied post the initial set of the GIC showed lower strengths.

Another study[28] evaluated the bonding of single-step SEA over unset GIC and set GIC at different intervals and compared the results to those of a TEA. It was concluded that the bond strength of the group where SEA was employed on unset GIC yielded the best results.

pH of self-etch adhesives

Zhang et al.[23] evaluated the microshear bond strengths (MSBS) of a TEA and four SEAs with different pH values when applied over two conventional GICs. All SEAs showed greater bond strengths than the total-etch group and no statistically significant difference was observed among the SEA groups. According to the authors, the harsh phosphoric acid etching in the total-etch group weakened the GIC surface by dissolution of the filler particles. Further, they also stated that the performance of the TEA might have been negatively influenced by insufficient solvent evaporation after its application or by the intrinsic water content of the set GIC.

Sharafeddin and Choobineh[30] evaluated the SBS using adhesives of different pH values and types where conventional GICs were used in the laminate technique. It was found that the SEAs resulted in higher SBS than TEA. Moreover, application of a mild SEA resulted in stronger bonds when compared to intermediate and strong SEA. The authors used the concepts of organic chemistry to explain that the invasion by a weak acid caused the least excitation and hence least salt crumps formation. Consequently, the unexcited cations were responsible for a strong ionic reaction with the adhesives. The results of this study were in accordance with another study[31] which also stated that the application of a mild SEA on unset GIC leads to superior bond strengths.

Resin-modified glass-ionomer cement and composite

Kasraie et al.[26] in their study compared the MSBS of composite and RMGIC using various bonding systems. They concluded that the self-etch systems performed better than the total-etch system. Two other studies[22],[24] where bond strength between RMGIC and composite was tested showed that SEAs resulted in greater bond strengths as compared to TEAs. The authors reasoned that the acidic nature of the SEA dissolves the surface of the RMGIC thereby improving the bond strength. Moreover, SEAs are less viscous, have a lesser contact angle, and hence, better wettability than TEAs.

Research[22],[27],[32] suggests that RMGIC can link with composites or bonding systems via a chemical bond formation of HEMA monomer by co-polymerization. This unreacted monomer is present in the air-inhibited layer of the superficial surface of the cured RMGIC. Moreover, a covalent chemical bond between bonding systems and the remaining monomer is also achieved in polyacid chains within the cured RMGIC.[33],[34]

The co-curing technique suggests the simultaneous curing of two different light-cured materials.[35] Knight[36] in their study suggested that co-curing RMGIC and composite together can lower the internal stress in composite restorations and also reduce the time required for the clinical procedure. Moreover, co-curing of RMGIC with composite results in a stronger bond between the two materials.[19]

Boruziniat and Gharaei[27] assessed the bond strength of RMGIC to composite using different adhesives and various curing methods. They concluded that SEAs showed better results than the total-etch group (P < 0.05). Upon co-curing, increased bond strengths were observed in the groups where self-etch bonding agents were used, unlike the total-etch group that showed decreased bond strengths. The authors reasoned that the uncured HEMA on the surface of RMGIC could enhance the wetting potential of bonding agents. The appearance of distinct resin tags observed in the scanning electron microscopic images of co-cured, two-step, SEA group could be attributed to their lower viscosity or the better wetting potential. The infiltration of resin into RMGICs could enhance their strength and therefore alter the failure mode. In the total-etch, co-cured group, etching was done before the development of the “resinous matrix” for its greater ingress into the resin-modified GIC. This impact of the TEA on uncured RMGIC was moderately comparable to the conventional GIC. The development of fragile salts on the surface of RMGIC,[31] elimination or reduction of calcium and aluminum ions leading to the lower tensile strength of RMGIC,[37] and a decrease in the HEMA content[32] could be the reasons for lower bond strengths in this group. Moreover, the authors concluded that the increased cohesive failures in this group were because of the weakening effect of the acid application on the uncured RMGIC structure.

Glass-ionomer cement versus resin-modified glass-ionomer cement

Pamir et al.[25] studied the outcome of various etching durations on the bond strength of composite to GICs and RMGICs and concluded that an etching time of 30 s was optimal for both the GIC types. They also compared the total-etch and self-etch bonding systems and concluded no statistically significant difference between the two for any time duration. RMGICs showed significantly better results than conventional GICs. The authors acknowledged the greater bond strengths between RMGIC and composite to a similarity in composition and curing mechanisms by free-radical initiator system.

Panahandeh et al.[29] studied the impact of time and type of adhesive application on the MSBS of composite to various GICs and RMGICs. The authors concluded that the variant (total-etch or self-etch) of adhesive had no influence on the results, but RMGICs performed better than the conventional GICs. According to them, the HEMA molecules within, along with the unreacted methacrylate groups, and the oxygen inhibition layer on the surface of RMGICs could lead to strong superior chemical covalent bonds with the adhesive resin, leading to better results.

Two articles were excluded from this systematic review as they included pretreatment of the GIC surface. Navimipour et al.[38] studied the effect of acid etching and Er, Cr: YSGG laser on the SBS of composite to GIC and RMGIC. They concluded that both the treatments led to better bond strengths in conventional GIC. However, among the RMGIC groups, better bond strengths were observed exclusively in the laser treatment group.

Otsuka et al.[39] carried out a study to determine how acid etching and air abrasion of GIC and RMGIC affected the bond strengths while using a SEA. Increased bond strengths were observed for conventional GIC, but the opposite was observed for RMGICs.

It is pertinent to state that there was a fair amount of variation in the mean bond strengths in the studies reviewed in this article. This can be advocated the different methodologies employed. Moreover, there was a disparity in the crosshead speed used while evaluating bond strengths. Studies indicate that samples tested at 0.5 mm/min showed remarkably better cohesive vs. adhesive results than other crosshead speeds.[40] SBS evaluated with crosshead speeds of 0.50 and 0.75 mm/min are more desirable.[41]

Limitations

Many studies were not comparable due to the different brands of materials used and a variation in the methodology employed.


  Conclusion Top


The use of SEAs resulted in superior bond strengths than total-etch bonding agents in the sandwich technique. Better results were obtained when SEA was employed on unset GIC in comparison to set GIC. Moreover, SEA applied over uncured RMGIC achieved better results as compared to cured RMGIC. Also, RMGICs due to the similarity in composition to composites fare reasonably better than conventional GICs in the sandwich technique.

Future implications

The success of the sandwich technique is primarily dependent on the bond strength of composite to GIC. SEAs are less technique sensitive and save ample chairside time. Hence, further exploration in the form of various clinical studies should be carried out.

Financial support and sponsorship

Nil.

Conflicts of interest

The authors of this manuscript declare that they have no conflicts of interest, real or perceived or financial or nonfinancial in this article.



 
  References Top

1.
Sidhu SK. Clinical evaluations of resin-modified glass-ionomer restorations. Dent Mater 2010;26:7-12.  Back to cited text no. 1
    
2.
Welbury RR, McCabe JF, Murray JJ, Rusby S. Factors affecting the bond strength of composite resin to etched glass-ionomer cement. J Dent 1988;16:188-93.  Back to cited text no. 2
    
3.
Akinmade AO, Nicholson JW. Glass-ionomer cements as adhesives. J Mater Sci 1993;4:95-101.  Back to cited text no. 3
    
4.
Forsten L. Short- and long-term fluoride release from glass ionomers and other fluoride-containing filling materials in vitro. Scand J Dent Res 1990;98:179-85.  Back to cited text no. 4
    
5.
Mickenautsch S, Mount G, Yengopal V. Therapeutic effect of glass-ionomers: An overview of evidence. Aust Dent J 2011;56:10-5.  Back to cited text no. 5
    
6.
Ngo H, Mount GJ, Peters MC. A study of glass-ionomer cement and its interface with enamel and dentin using a low-temperature, high-resolution scanning electron microscopic technique. Quintessence Int 1997;28:63-9.  Back to cited text no. 6
    
7.
Wilson AD. Resin-modified glass-ionomer cements. Int J Prosthodont 1990;3:425-9.  Back to cited text no. 7
    
8.
Xie D, Brantley WA, Culbertson BM, Wang G. Mechanical properties and microstructures of glass-ionomer cements. Dent Mater 2000;16:129-38.  Back to cited text no. 8
    
9.
Robertello FJ, Coffey JP, Lynde TA, King P. Fluoride release of glass ionomer-based luting cements in vitro. J Prosthet Dent 1999;82:172-6.  Back to cited text no. 9
    
10.
Khoroushi M, Keshani F. A review of glass-ionomers: From conventional glass-ionomer to bioactive glass-ionomer. Dent Res J (Isfahan) 2013;10:411-20.  Back to cited text no. 10
    
11.
Sneed WD, Looper SW. Shear bond strength of a composite resin to an etched glass ionomer. Dent Mater 1985;1:127-8.  Back to cited text no. 11
    
12.
Naughton WT, Latta MA. Bond strength of composite to dentin using self-etching adhesive systems. Quintessence Int 2005;36:259-62.  Back to cited text no. 12
    
13.
Barkmeier WW, Shaffer SE, Gwinnett AJ. Effects of 15 vs 60 second enamel acid conditioning on adhesion and morphology. Oper Dent 1986;11:111-6.  Back to cited text no. 13
    
14.
Mangum FI, Berry EA 3rd, Parikh UK, Ladd D. Optimal etching time of glass ionomer cement for maximum bond of composite resin. J Am Dent Assoc 1990;120:535-8.  Back to cited text no. 14
    
15.
Sensi LG, Lopes GC, Monteiro S Jr., Baratieri LN, Vieira LC. Dentin bond strength of self-etching primers/adhesives. Oper Dent 2005;30:63-8.  Back to cited text no. 15
    
16.
De Munck J, Van Landuyt K, Peumans M, Poitevin A, Lambrechts P, Braem M, et al. A critical review of the durability of adhesion to tooth tissue: Methods and results. J Dent Res 2005;84:118-32.  Back to cited text no. 16
    
17.
Lührs AK, Guhr S, Schilke R, Borchers L, Geurtsen W, Günay H. Shear bond strength of self-etch adhesives to enamel with additional phosphoric acid etching. Oper Dent 2008;33:155-62.  Back to cited text no. 17
    
18.
McLean JW, Powis DR, Prosser HJ, Wilson AD. The use of glass-ionomer cements in bonding composite resins to dentine. Br Dent J 1985;158:410-4.  Back to cited text no. 18
    
19.
Zanata RL, Navarro MF, Ishikiriama A, da Silva e Souza Júnior MH, Delazari RC. Bond strength between resin composite and etched and non-etched glass ionomer. Braz Dent J 1997;8:73-8.  Back to cited text no. 19
    
20.
Lopes GC, Marson FC, Vieira LC, de Caldeira AM, Baratieri LN. Composite bond strength to enamel with self-etching primers. Oper Dent 2004;29:424-9.  Back to cited text no. 20
    
21.
Gopikrishna V, Abarajithan M, Krithikadatta J, Kandaswamy D. Shear bond strength evaluation of resin composite bonded to GIC using three different adhesives. Oper Dent 2009;34:467-71.  Back to cited text no. 21
    
22.
Arora V, Kundabala M, Parolia A, Thomas MS, Pai V. Comparison of the shear bond strength of RMGIC to a resin composite using different adhesive systems: An in vitro study. J Conserv Dent 2010;13:80-3.  Back to cited text no. 22
[PUBMED]  [Full text]  
23.
Zhang Y, Burrow MF, Palamara JE, Thomas CD. Bonding to glass ionomer cements using resin-based adhesives. Oper Dent 2011;36:618-25.  Back to cited text no. 23
    
24.
Chandak MG, Pattanaik N, Das A. Comparative study to evaluate shear bond strength of RMGIC to composite resin using different adhesive systems. Contemp Clin Dent 2012;3:252-5.  Back to cited text no. 24
[PUBMED]  [Full text]  
25.
Pamir T, Sen BH, Evcin O. Effects of etching and adhesive applications on the bond strength between composite resin and glass-ionomer cements. J Appl Oral Sci 2012;20:636-42.  Back to cited text no. 25
    
26.
Kasraie S, Shokripour M, Safari M. Evaluation of micro-shear bond strength of resin modified glass-ionomer to composite resins using various bonding systems. J Conserv Dent 2013;16:550-4.  Back to cited text no. 26
[PUBMED]  [Full text]  
27.
Boruziniat A, Gharaei S. Bond strength between composite resin and resin modified glass ionomer using different adhesive systems and curing techniques. J Conserv Dent 2014;17:150-4.  Back to cited text no. 27
[PUBMED]  [Full text]  
28.
Gupta R, Mahajan S. Shear bond strength evaluation of resin composite bonded to GIC using different adhesives. J Clin Diagn Res 2015;9:ZC27-9.  Back to cited text no. 28
    
29.
Panahandeh N, Torabzadeh H, Ghassemi A, Mahdian M, Akbarzadeh Bagheban A, Moayyedi S. Effect of bonding application time on bond strength of composite resin to glass ionomer cement. J Dent (Tehran) 2015;12:859-67.  Back to cited text no. 29
    
30.
Sharafeddin F, Choobineh MM. Assessment of the shear bond strength between nanofilled composite bonded to glass-ionomer cement using self-etch adhesive with different pHs and total-etch adhesive. J Dent (Shiraz) 2016;17:1-6.  Back to cited text no. 30
    
31.
Kandaswamy D, Rajan KJ, Venkateshbabu N, Porkodi I. Shear bond strength evaluation of resin composite bonded to glass-ionomer cement using self-etching bonding agents with different pH: In vitro study. J Conserv Dent 2012;15:27-31.  Back to cited text no. 31
[PUBMED]  [Full text]  
32.
Kerby RE, Knobloch L. The relative shear bond strength of visible light-curing and chemically curing glass-ionomer cement to composite resin. Quintessence Int 1992;23:641-4.  Back to cited text no. 32
    
33.
Farah CS, Orton VG, Collard SM. Shear bond strength of chemical and light-cured glass ionomer cements bonded to resin composites. Aust Dent J 1998;43:81-6.  Back to cited text no. 33
    
34.
Oilo G, Um CM. Bond strength of glass-ionomer cement and composite resin combinations. Quintessence Int 1992;23:633-9.  Back to cited text no. 34
    
35.
Knight GM, McIntyre JM, Mulyani. Bond strengths between composite resin and auto cure glass ionomer cement using the co-cure technique. Aust Dent J 2006;51:175-9.  Back to cited text no. 35
    
36.
Knight GM. The co-cured, light-activated glass-ionomer cement-composite resin restoration. Quintessence Int 1994;25:97-100.  Back to cited text no. 36
    
37.
Leirskar J, Nordbø H, Mount GJ, Ngo H. The influence of resin coating on the shear punch strength of a high strength auto-cure glass ionomer. Dent Mater 2003;19:87-91.  Back to cited text no. 37
    
38.
Navimipour EJ, Oskoee SS, Oskoee PA, Bahari M, Rikhtegaran S, Ghojazadeh M. Effect of acid and laser etching on shear bond strength of conventional and resin-modified glass-ionomer cements to composite resin. Lasers Med Sci 2012;27:305-11.  Back to cited text no. 38
    
39.
Otsuka E, Tsujimoto A, Takamizawa T, Furuichi T, Yokokawa M, Tsubota K, et al. Influence of surface treatment of glass-ionomers on surface free energy and bond strength of resin composite. Dent Mater J 2013;32:702-8.  Back to cited text no. 39
    
40.
Lindemuth JS, Hagge MS. Effect of universal testing machine crosshead speed on the shear bond strength and bonding failure mode of composite resin to enamel and dentin. Mil Med 2000;165:742-6.  Back to cited text no. 40
    
41.
Hara AT, Pimenta LA, Rodrigues AL Jr. Influence of cross-head speed on resin-dentin shear bond strength. Dent Mater 2001;17:165-9.  Back to cited text no. 41
    


    Figures

  [Figure 1]
 
 
    Tables

  [Table 1], [Table 2]



 

Top
 
 
Search
Similar in PUBMED
   Search Pubmed for
   Search in Google Scholar for
 Related articles
Access Statistics
Email Alert *
Add to My List *
* Registration required (free)  

 
  In this article
Abstract
Introduction
Materials and Me...
Results and Disc...
Conclusion
References
Article Figures
Article Tables

 Article Access Statistics
    Viewed354    
    Printed12    
    Emailed0    
    PDF Downloaded68    
    Comments [Add]    

Recommend this journal