|Year : 2022 | Volume
| Issue : 1 | Page : 32
Evaluation of the effects of different concentrations of bleaching agents on flexural strength and microhardness of VITA ENAMIC
Mahshid Shakibafard1, Fariba Ezoji2, Behnaz Esmaeili2, Ali Bijani3
1 Dentist, Tehran, Iran
2 Dental Materials Research Center, Health Research Institute, Babol University of Medical Sciences, Babol, Iran
3 Social Determinants of Health Center, Health Research Institute, Babol University of Medical Sciences, Babol, Iran
|Date of Submission||29-Sep-2020|
|Date of Acceptance||07-Dec-2021|
|Date of Web Publication||27-Apr-2022|
Dr. Behnaz Esmaeili
Department of Restorative Dentistry, Faculty of Dentistry, Babol University of Medical Sciences, Babol
Source of Support: None, Conflict of Interest: None
Background: Considering the studies on the effects of bleaching materials on properties of dental materials, The aims of this in vitro study were to evaluate the effects of two different concentrations of bleaching agents on flexural strength and microhardness of VITA ENAMIC.
Materials and Methods: In this experimental in vitro study, 30 rectangular-shaped specimens (2 mm width × 2 mm height × 12 mm length) for flexural strength and 30 specimens (5 mm width × 5 mm length × 2 mm height) for microhardness tests were prepared from VITA ENAMIC blocks 12 × 14 × 18 mm. The specimens were polished using silicon-carbide sandpapers 400, 600, 800, 1200, 2000 under flow of water for 60 s each. The prepared samples for flexural strength and microhardness were divided into 3 subgroups (n = 10): control group (C), samples bleached using Opalescence PF 15% (B15), and samples bleached with Opalescence Xtra Boost 40% (B40). Flexural strength measurement was done using a universal testing machine, and microhardness test was done using Vickers. Data were analyzed using analysis of variance and post hoc tests and P < 0.05 was considered significant.
Results: The mean microhardness values of C, B15, and B40 groups were 255.46 ± 3.02, 249.86 ± 4.18, and 235.53 ± 4.61 kgf/mm2. Opalescence PF 15% and Opalescence Xtra Boost 40% affected microhardness of ENAMIC significantly (P < 0.05). The mean flexural strength values of C, B15, and B40 groups were 155.26 ± 16.13, 142.14 ± 11.52, and 133.39 ± 16.13 MPa. A significant decrease in flexural strength was found between the C and B40 groups (P = 0.007). However, the difference between flexural strength of the C and B15 groups was not significant (P > 0.05).
Conclusion: Our study showed that both concentrations of bleaching agents can affect microhardness of ENAMIC. Moreover, hydrogen peroxide 40% has a negative effect on the flexural strength of ENAMIC.
Keywords: Bleaching agents, flexural strength, hardness, VITA ENAMIC
|How to cite this article:|
Shakibafard M, Ezoji F, Esmaeili B, Bijani A. Evaluation of the effects of different concentrations of bleaching agents on flexural strength and microhardness of VITA ENAMIC. Dent Res J 2022;19:32
|How to cite this URL:|
Shakibafard M, Ezoji F, Esmaeili B, Bijani A. Evaluation of the effects of different concentrations of bleaching agents on flexural strength and microhardness of VITA ENAMIC. Dent Res J [serial online] 2022 [cited 2022 May 23];19:32. Available from: https://www.drjjournal.net/text.asp?2022/19/1/32/344155
| Introduction|| |
Achievement of a healthy, natural, and beautiful smile is one of the most important issues in restorative dentistry. Besides other techniques, bleaching is a conservative option to improve the color of stained or darkened teeth., At home and in office bleaching are two common methods of bleaching technique., Different materials and concentrations are used for bleaching procedure such as carbamide peroxide and hydrogen peroxide.,,
Effects of bleaching agents on teeth depend on various options such as their concentration, bleaching time, and type of stain., Bleaching procedure works through oxidation-reduction reactions which change the chemical molecular structure of stains and result in tooth whitening.
Dental ceramics are widely used in restorative dentistry due to their mechanical and esthetic properties. One of the most important properties of dental ceramics is their chemical survival when exposed to saliva and substances with different pH. Ceramic restorations can be designed and created in dental laboratories or with the help of computer-aided design/computer-aided manufacturing (CAD/CAM) technology.
CAD/CAM technology results in materials with higher qualities. Moreover, less amount of time is needed for their creation., Developing new materials for CAD/CAM systems to combine proper characteristics of ceramics such as color stability and durability with improved flexural strength and low abrasiveness of composites has led to production of recent materials like VITA ENAMIC.
VITA ENAMIC is the first hybrid dental ceramic which has a three-dimensional geometry with two penetration networks. One network is a glass-ceramic material and the other is a polymer (methacrylate) which reinforces the glass-ceramic network. The two networks have high flexural strength. VITA ENAMIC can absorb mastication forces by balancing between elasticity and flexural strength. VITA ENAMIC can be used for long-term restorations in the anterior and lateral areas, such as full-coverage crowns, veneers, inlays, and onlays.
During bleaching procedure, dental ceramics are exposed to bleaching materials. Therefore, their effect on physical and mechanical properties of ceramics has been considerable.
Every year, various studies are conducted on the effects of bleaching agents on properties of restorative materials. Results of some studies are contradictory. Culic et al. reported that Opalescence PF 15% did not affect surface structure of VITA ENAMIC. Poludorou et al. claimed in a paper that carbamide peroxide 15% did not affect the microhardness of Vitablocs Mark II ceramic, while Malkondu et al. showed in a research that 20% carbamide peroxide decreased the microhardness of EMPRESS esthetic ceramic.
Evaluation of different effects of bleaching agents on VITA ENAMIC is important due to desirable properties of VITA ENAMIC and increasing use of this dental material in recent years.
The purpose of this in vitro study was to evaluate the effects of 2 different concentrations of bleaching agents on flexural strength and microhardness of VITA ENAMIC.
| Materials and Methods|| |
Preparation of samples
In this experimental in vitro study, 30 rectangular-shaped specimens 2/2/12 mm10 for flexural strength test and 30 specimens 5/2/2 mm for microhardness test were prepared from 6 VITA ENAMIC (VITA Zahnfabrik/Germany) blocks 12/14/18 mm. VITA ENAMIC blocks were sectioned using Delta precision sectioning machine (Nemo/Mashhad, Iran) at low speed. The prepared specimens were polished using silicon-carbide sandpapers 400, 600, 800, 1200, 2000 under flow of water for 60 s each.
The prepared samples for flexural strength and microhardness tests were divided into 3 subgroups.
These specimens were bleached using Opalescence PF 15% (Ultradent/USA) for 14 days, each day 4 h according to the Manufacturer's instructions. During bleaching procedure, specimens were kept in 37°C humid environment in incubator (LTE scientific LTD/Greenfield, Great Britain). Samples were kept in distilled water between bleaching sessions.
These specimens were bleached using Opalescence Xtra Boost 40% (Ultradent/USA) in 2 sessions 1 week apart, every session 3 times, each time 20 min. Bleaching gel was applied on samples surface. After 20 min, the samples were washed for 30 s. After drying the samples, a new layer of bleaching gel was applied. This procedure was repeated 3 times in each session. Samples were kept in distilled water between bleaching sessions.
Control group samples were kept in distilled water during the procedure and were not bleached.
Flexural strength test
Flexural strength test for all the prepared samples for this test was done using a universal testing machine (koopa pazhoohesh/sari, Iran). Three point bending test was used for measuring flexural strength of prepared samples.
The sample was placed on two supports with the bleaching surface facing the machine's crosshead. There was 10 mm space between the two supports. Crosshead speed was 1.0 mm/min. Loading continued until the sample fractured. Width and height of the sample at the fracture point were measured using digital caliper (Shinwa sokutei/China).
Flexural strength values were calculated using the following equation:
Where F is the failure load (in N), L is the distance between the supports (in mm)
B and H are the width and height of fractured points (all in mm).
Microhardness test for all the prepared samples for this test was done using Vickers (koopa pazhoohesh, sari, Iran). 300 g force was applied to the samples. Loading time was 30 s. Microhardness was measured in 3 points. The calculated average microhardness of these 3 points was reported as the sample's microhardness.
The mean microhardness and flexural strength were calculated for all groups. Data were analyzed using SPSS statistical software package SPSS 17.0 for Windows (SPSS, Chicago, Illinois, USA). Data were analyzed using analysis of variance and post hoc tests. P < 0.05 was considered significant.
| Results|| |
Mean Vickers hardness values of VITA ENAMIC and mean flexural strength values are shown in [Table 1].
|Table 1: The mean microhardness and flexural strength values of enamic (with standard deviation)|
Click here to view
The mean (standard deviation) microhardness values of C, B15, and B40 groups were 255.46 ± 3.02, 249.86 ± 4.18, and 235.53 ± 4.61 kgf/mm2, respectively.
A statistically significant difference in microhardness between control group and VITA ENAMIC bleached with opalescence pf 15% (P = 0.011) and opalescence Xtra Boost 40% (P < 0.001) was found.
Furthermore, the difference between microhardness values of VITA ENAMIC bleached with opalescence pf 15% and opalescence Xtra Boost 40% was significant (P < 0.001).
The mean (standard deviation) flexural strength values of C, B15, and B40 groups were 155.26 ± 16.13, 142.14 ± 11.52, and 133.39 ± 16.13 MPa.
There was a statistically significant difference between the flexural strength values of the control group and VITA ENAMIC bleached with opalescence Xtra Boost 40% (P = 0.007).
However, the difference between the control group and VITA ENAMIC bleached with opalescence pf 15% was not significant (P = 0.135) as between flexural strength of samples bleached with opalescence pf 15% and opalescence Xtra Boost 40% (P = 0.394). [Figure 1] and [Figure 2] present the mean microhardness and mean flexural strength of VITA ENAMIC.
|Figure 1: The mean microhardness of VITA ENAMIC (kgf/mm2) different letters (a, b, c) represent statistically significant difference.|
Click here to view
|Figure 2: The mean flexural strength of VITA ENAMIC (MPa) different letters (a, b) represent statistically significant difference.|
Click here to view
| Discussion|| |
Maintenance of dental restorations that are exposed to saliva and other substances are affected by mechanical properties of restorative materials such as flexural strength and microhardness. Nowadays, bleaching procedure is a common treatment in dental offices. While bleaching procedure, bleaching materials may come in contact with dental restorations and crowns in the mouth. This research was conducted to observe the effects of two different bleaching agents on VITA ENAMIC material.
The results of this study showed a significant decrease in microhardness of VITA ENAMIC after bleaching with opalescence pf 15% and Opalescence Xtra Boost 40%.
VITA ENAMIC has two networks which one of these networks is a polymer (methacryl). In this study, a reduction in microhardness of VITA ENAMIC was expected due to oxidization of resin matrix by the bleaching materials. Some studies reported a decrease in microhardness of methacrylate-based composites after bleaching with carbamide peroxide., Juntavee et al. declared in a study that 35% hydrogen peroxide reduces hardness of ENAMIC significantly. These results are consistent with the results of our study. This microhardness decrease is due to polymer chains cleavage by bleaching gels containing peroxides. Carbamide peroxide decomposes into hydrogen peroxide and urea. Hydrogen peroxide breaks into free radicals. and these free radicals break down polymer chains. Another factor that reduces the microhardness is increased softening of composite resins due to existence of some monomers. These monomers make composites more susceptible to bleaching gels. In our study also, the difference between microhardness of bleached specimens was statistically significant and the values were more decreased in specimens bleached with Opalescence Xtra Boost 40%. This explains that bleaching effect on microhardness of VITA ENAMIC is concentration dependent. Malkondu et al. suggested that effect of bleaching gels on microhardness of materials is concentration dependent. This finding is in accordance with our study. This result might be because of the fact that when the concentration gets higher, the penetration depth and dissolution effect of bleaching agent increases and the effect on surface properties becomes higher. Thus, the bleaching agent will have a greater effect on surface properties of dental material.
Türker and Biskin declared that 10% and 16% carbamide peroxide decreased microhardness of feldspathic porcelain. A decrease in SIO2 content in feldspathic porcelain after bleaching affected the surface hardness and decreased the microhardness. As SIO2 is one of the important components in VITA ENAMIC, reduction of SIO2 content can be another reason for the decrease seen in microhardness of VITA ENAMIC after bleaching.
Furthermore, they are some articles with conflicting results. In Bahannan's research, 10%, 20%, and 35% carbamide peroxide did not affect the microhardness of feldspathic porcelain. This may be due to different structure of feldspathic porcelain and VITA ENAMIC, different fabrication method, and the fact that VITA ENAMIC is a hybrid ceramic and has a methacryl network. In another research, Demir et al. observed that 16% carbamide peroxide had no significant effect on microhardness of IPS Empress CAD and IPS emax CAD. This conflicting result might be because of different concentrations of bleaching gel used, different ceramics to VITA ENAMIC, and different durations which bleaching gels were used.
In this study, a statistically significant decrease was found in flexural strength of VITA ENAMIC after bleaching with Opalescence Xtra Boost 40%. However, the decrease in flexural strength of specimens bleached with Opalescence PF 15% was not significant. Furthermore, there was no statistically significant difference between flexural strength of specimens bleached with Opalescence Xtra Boost 40% and opalescence pf 15%. Flexural strength is especially notable where intense occlusal stresses are applied such as in long-span fixed dental prosthesis.
It was suggested in a study that 16% carbamide peroxide did not affect the flexural strength of composite resins and it was declared that filler particles, the chemical bondblocks promoted by coupling agents at the interface of resin-filler were some factors that prevented the expansion of cracks in composites during flexural strength test. This finding is similar to our results. As VITA ENAMIC is a hybrid ceramic, this can explain why flexural strength of VITA ENAMIC did not change significantly after bleaching with Opalescence PF 15%. In another study, Hao got the same results after bleaching VITA mark II with opalescence pf 15%. Moreover, no changes were observed in flexural strength of this ceramic after bleaching. Furthermore, there are some studies with contrary results. A study concluded that 15% carbamide peroxide significantly decreased the flexural strength of Z250 micro-hybrid composite resin due to the effect of free radicals of the bleaching agent on the resin section of the material.
In general, the conflicting results may be due to properties of the studied materials., Moreover, other factors may be concentration of bleaching gels and the period of time that they are applied to the materials.
According to our study, bleaching agents can affect microhardness of VITA ENAMIC. Moreover, hydrogen peroxide 40% affects the flexural strength of VITA ENAMIC. Hence, the clinicians should prevent the bleaching gel from coming into contact with VITA ENAMIC restorations.
The limitation is that saliva and mastication forces are absent in our study. These factors may affect VITA ENAMICs respond to bleaching gels. Furthermore, volume loss from VITA ENAMIC surface was not noticed. Further researches can investigate the effects of bleaching gels on the properties of VITA ENAMIC in the presence of saliva and mastication forces in an in vivo study. Furthermore, effect of polishing on alternation of VITA ENAMIC's properties after bleaching can be investigated in further studies.
| Conclusion|| |
- The microhardness of VITA ENAMIC decreased after bleaching procedure using Opalescence PF 15% or Opalescence Xtra Boost 40%
- The effects of bleaching materials on microhardness of VITA ENAMIC was concentration dependent
- The flexural strength of VITA ENAMIC decreased after bleaching with Opalescence Xtra Boost 40%
- Opalescence PF 15% did not affect flexural strength of VITA ENAMIC
- No significant differences were observed between flexural strength of VITA ENAMIC bleached with opalescence pf 15% and opalescence Xtra Boost 40%.
The authors would like to thank Dental materials Research Center and Research Council of Babol University of Medical Sciences.
Financial support and sponsorship
Babol university of medical sciences.
Conflicts of interest
The authors of this manuscript declare that they have no conflicts of interest, real or perceived, financial or nonfinancial in this article.
| References|| |
Malkondu Ö, Yurdaguven H, Say E, Kazazoglu E, Soyman M. Effect of bleaching on microhardness of esthetic restorative materials. Oper Dent 2011;36:177-86.
Ural C, Gencer Y, Tarakci M, Aslan M, Arici S, Tatar N. Effect of bleaching agents on surface texture of feldespathic ceramic. J Exp Clin Med 2014;31:177-81.
Silva FB, Chisini LA, Demarco FF, Horta BL, Correa MB. Desire for tooth bleaching and treatment performed in Brazilian adults: Findings from a birth cohort. Braz Oral Res 2018;32:e12.
Polydorou O, Hellwig E, Auschill TM. The effect of different bleaching agents on the surface texture of restorative materials. Oper Dent 2006;31:473-80.
Şişmanoğlu S. An overview of vital tooth bleaching. J Health Sci 2020;2:115-39.
Bahannan S. Effects of different bleaching agent concentrations on surface roughness and microhardness of esthetic restorative materials. Saudi J Dent Res 2015;6:124-8.
Ranjbar Omrani L, Khoshamad S, Tabatabaei Ghomshe E, Chiniforush N, Hashemi Kamangar SS. In vitro
effect of bleaching with 810 nm and 980 nm diode laser on microhardness of self-cure and light-cure glass ionomer cements. J Lasers Med Sci 2017;8:191-6.
Ourique S, Arrais C, Cassoni A, Tsuzuki C, Rodrigues J. Effects of different concentrations of carbamide peroxide and bleaching periods on the roughness of dental ceramics. Braz Oral Res 2011;25:453-8.
Berger SB, Pazenhagen R, Martinelli N, Moura SK, Carvalho RV, Guiraldo RD. Effect of bleaching agents on the flexural strength of bovine dentin. J Contemp Dent Pract 2014;15:552-5.
Yu H, Li Q, Lin Y, Buchalla W, Wang Y. Influence of carbamide peroxide on the flexural strength of tooth-colored restorative materials: An in vitro
study at different environmental temperatures. Oper Dent 2010;35:300-7.
Culic B, Gasparik C, Varvara M, Culic C, Dragos C, Silaghi L, et al
. Evaluation of bleaching on a CAD/CAM hybrid ceramic material. Stud UBB Chem 2017;1:61-71.
Lim CH, Jang YS, Lee MH, Bae TS. Evaluation of fracture strength for single crowns made of the different types of lithium disilicate glass-ceramics. Odontology 2020;108:231-9.
Dirxen C, Blunck U, Preissner S. Clinical performance of a new biomimetic double network material. Open Dent J 2013;7:118-22.
Polydorou O, Hellwig E, Auschill TM. The effect of at-home bleaching on the microhardness of six esthetic restorative materials. J Am Dent Assoc 2007;138:978-84.
Hatanaka GR, Abi-Rached Fde O, Almeida-Júnior AA, Cruz CA. Effect of carbamide peroxide bleaching gel on composite resin flexural strength and microhardness. Braz Dent J 2013;24:263-6.
Esmaeili B, Abolghasemzadeh F, Gholampor A, Daryakenari G. The effect of home bleaching carbamide peroxide concentration on the microhardness of dental composite resins. Gen Dent 2018;66:40-4.
Kamangar SS, Kiakojoori K, Mirzaii M, Fard MJ. Effects of 15% carbamide peroxide and 40% hydrogen peroxide on the microhardness and color change of composite resins. J Dent (Tehran) 2014;11:196-209.
Juntavee N, Juntavee A, Saensutthawijit P. Influences of light-emitting diode illumination bleaching technique on nanohardness of computer-aided design and computer-aided manufacturing ceramic restorative materials. J Contemp Dent Pract 2018;19:196-204.
Türker SB, Biskin T. The effect of bleaching agents on the microhardness of dental aesthetic restorative materials. J Oral Rehabil 2002;29:657-61.
Rosentritt M, Lang R, Plein T, Behr M, Handel G. Discoloration of restorative materials after bleaching application. Quintessence Int 2005;36:33-9.
Demir N, Karci M, Ozcan M. Effects of 16% carbamide peroxide bleaching on the surface properties of glazed glassy matrix ceramics. Biomed Res Int 2020;2020:1864298.
Braga R. Craig's Restorative Dental Materials. 14th
ed. St. Louis: Mosby Co.; 2019.
Kimyai S, Ghavami Lahij Y, Daneshpooy M, Jafari Navimipour E, Alizadeh Oskoee P. Effect of bleaching with 15% carbamide peroxide on flexural strength of three resin-based restorative materials. Front Dent 2020;17:27.
[Figure 1], [Figure 2]