ORIGINAL ARTICLE
Year : 2022  |  Volume : 19  |  Issue : 1  |  Page : 62

The effect of multiple enamel conditioning on enamel micro-hardness


1 Department of Orthodontics, Orthodontics Research Center, School of Dentistry, Shiraz University of Medical Sciences, Shiraz, Iran
2 Department of Orthodontics, Dental Research Center, Dental Research Institute, School of Dentistry, Isfahan University of Medical Sciences, Isfahan, Iran

Date of Submission05-May-2021
Date of Acceptance30-Oct-2021
Date of Web Publication16-Aug-2022

Correspondence Address:
Dr. Shabnam Ajami
School of Dentistry, Qom Abad, Ghasrodasht St. Shiraz, Shiraz
Iran
Login to access the Email id

Source of Support: None, Conflict of Interest: None


DOI: 10.4103/1735-3327.353831

Rights and Permissions
  Abstract 


Background: White spot formation is one of the common side effects in orthodontic treatments and multiple enamel conditioning might happen even during on session of fixed orthodontic treatments. The aim of the present study was to evaluate the impact of multiple enamel conditioning with different methods on enamel micro-hardness (MH).
Materials and Methods: In this In vitro experimental study, the buccal surfaces of 105 extracted premolars were evaluated in seven groups: One control and six experimental groups. The enamel conditioning was performed in three ways: Etching with phosphoric acid 37%, etching with phosphoric acid 37% followed by primer application and conditioning with self-etch primer. The conditioning process in each way was also performed twice consecutively. The specimens were submitted in pH cycling model with demineralization and re-mineralization solutions for 14 days. Afterward Vickers MH test was applied with 0.981N force on the teeth for 10 s indentation time. Data were analyzed using One-Way ANOVA and Tukey HSD (honestly significant difference) test for multiple comparisons. A value of P < 0.05 was considered statistically significant.
Results: MH analysis showed statistically significant differences between the control group and the other conditioned groups (P < 0.05). The groups conditioned with acid-etch and primer, particularly twice, showed the lowest amount of MH in comparison to other groups. Self-etch primer had the least effect on MH of the enamel. Single time etching without using primer, made no considerable difference when compared to multiple etching.
Conclusion: Etching process and covering the enamel with primer decrease enamel MH. Using self-etch primer is a more conservative method of enamel conditioning.

Keywords: Dental caries, dental tissue conditioning, hardness, tooth demineralization


How to cite this article:
Salehi P, Shavakhi M, Nazari S, Ajami S. The effect of multiple enamel conditioning on enamel micro-hardness. Dent Res J 2022;19:62

How to cite this URL:
Salehi P, Shavakhi M, Nazari S, Ajami S. The effect of multiple enamel conditioning on enamel micro-hardness. Dent Res J [serial online] 2022 [cited 2022 Oct 4];19:62. Available from: https://www.drjjournal.net/text.asp?2022/19/1/62/353831




  Introduction Top


Fixed orthodontic appliances need to be bonded to the enamel surface. This process is a preliminary step of fixed orthodontic treatments. The conventional method of bonding procedure includes surface treatment of the enamel by etching with phosphoric acid to achieve micro-retentions.[1] Another method for bonding the brackets is using self-etch primers which consists of conditioner and priming agents.[2] The phosphate group in self-etch primers dissolves the calcium bonded to hydroxyapatite. The dissolved calcium bonds to the phosphate group and forms the network during polymerization.[3] One of the flaws of these methods is bracket attachment failure. It can be due to inappropriate forces exerted to the brackets by patients during masticatory functions, or because of the poor bonding technique. Moreover, bracket repositioning might be needed at bonding appointments or later. Therefore, re-etching and re-bonding of the enamel surface might be mandatory several times.[4]

White spot lesion formation is a common clinical problem in orthodontic patients.[5] These lesions are the first manifestations of enamel decalcification and can affect the esthetic aspects of the orthodontic treatments,[6] and cause dissatisfaction, particularly for those who demand facial and dental esthetics.[7] Moreover, white spot lesion is the primary stage of enamel demineralization and in case of poor oral hygiene can lead to enamel caries which necessitates restorative treatments.[8] White spot lesions can also be initiated iatrogenically; Mechanical or chemical damages to enamel increase the permeability of enamel and consequently can increase susceptibility to demineralization and caries.[9] It has been shown that increasing the etching duration and exceeding the area beyond the bracket bases[10] trigger the white spot formation. Furthermore, etching the enamel particularly more than five times increases surface permeability significantly.[9] On the other hand, nonrinse conditioners prepare a smooth and adequately rough surface on enamel[11] and produce more conservative retentive patterns in enamel structure than conventional etch and rinse agents.[12]

Multiple enamel etching due to poor bracket position or bonding failures is common in fixed orthodontic treatments and this process may increase the susceptibility of enamel to white spot lesion formation which decreases enamel micro-hardness (MH). Although etching the whole enamel surface seems to be harmful, covering the surplus etched area with adhesive is recommended.[10] On the other hand, it has been claimed that under the clinical circumstance where fluoride is used regularly, extending the etched area would not be a problem.[13] In the present study, we aimed to evaluate the effect of multiple conditioning of the enamel with self-etch and conventional etch-and-rinse method on the MH of enamel sites beyond the bonding area beneath the brackets.


  Materials and Methods Top


In this in-vitro experiment, a total of 105 premolar teeth were collected after extraction for orthodontic purposes. The exclusion criteria were as follows: Existence of carious lesions, history of fixed orthodontic treatment, etching or restorative treatment, presence of white spot lesions or any developmental enamel defects, cracks due to the extraction procedure or exposure to any chemical solutions like hydrogen peroxide. To prevent demineralization the specimens were stored in tap water (21°C) for 2 weeks before the trial.

The roots of the teeth were cut from the cemento-enamel junction by diamond disc (Jota, Germany). The remained crowns were mounted in the 1 cm × 1.1 × cm 1 cm3 cube of self-cure acrylic blocks (Akropars, Iran). They were polished by fine handpiece acryl rubber (Jota, Germany) and followed by fine silicon carbide polishing paper (Matador-Germany-P: 1000), preparing a flat surface for the Vickers test.

The samples were allocated to seven trial groups (n = 15 each). The groups were as follows: (1) No procedure was applied on the enamel surface (control group). (2) The enamel surfaces were etched once. The samples of group 2 of the enamel conditioning process were etching with 37% phosphoric acid (3M ESPE Etching Liquid 1923-USA) for 15 sec, rinsing with water for 30 s, and drying with oil-free dry air for 20 s. (3) The same etching procedure as Group 2 was performed two times consecutively. (4) The teeth were etched the same as Group 2 and then primer (Transbond XT, 3M, Unitek) was applied as a thin uniform coat and cured for 10 s from the buccal surface direction with an LED curing unit (Elipar S10, 3M-ESPE, Seefeld, Germany, 1200 mw/cm2, 430–480 nm) immediately. (5) The same procedure as the fourth group was done for two times. The buccal surface of the teeth was polished with adhesive removal finishing bur (G and H orthodontics, USA) after the first etch and primer applying procedure. (6) The enamel surfaces were conditioned with self-etch primer (Transbond Plus self-etch system, 3M, Unitek) for 5 s. Then, it was cured for 10 s from the buccal direction with an LED curing unit immediately. (7) The same procedure as the sixth group was done two times. The buccal surfaces of the teeth were polished with adhesive removal carbide bur (G and H orthodontics, USA) after the first self-etch primer application.

Then, all specimens were submitted to the dynamic demineralization and re-mineralization cycling model proposed by O'reilly,[14] with the solutions proposed by Argenta.[15] The pH-cycling challenge consists of immersing the specimens in a demineralization solution (2.0 mmol/L of calcium, 2.0 mmol/L of phosphate, and 75 mmol/L of acetate in pH 4.5) for 6 h, followed by rinsing in deionized water, drying with air-jet and immersing in a re-mineralization solution (1.5 mmol/L of calcium, 0.9 mmol/L of phosphate, 150 mmol/L of potassium chloride, and 20 mmol/L of Tris buffer at pH 7.0), for 18 h at 37°C. The entire procedure was repeated daily for 14 days, and the solutions were changed on a 5-day cycle period.

After pH cycling, the samples were tested for transversal MH measurements. Hardness is defined as the resistance to permanent surface indentation or penetration.[16] The Vickers hardness test uses a square-based diamond indenter. The indenter is a 136° diamond-shaped indenter which forces into the material with a definite load application.[16] Transversal Vickers hardness (MHV 10002, SCTMC, china) was performed with 0.981 N forces on the teeth for 10 s indentation time. Each measurement was conducted three times with 50 μm distance from each other. Indentations were evaluated with infinite focus microscope (Alicona Imaging, Grambach, Austria) measuring longitudinal and transverse axes of the indents (d1, d2 [μm]). Vickers hardness number (HV) was calculated using the following equation: HV = 0.102 × 2× sin (136/2) × (F/d2), with d = (d1 + d2)/2.

Statistical analysis was performed using SPSS 19 software (SPSS, Chicago, Ill). To evaluate the impact of method types and times of enamel conditioning on Log e MH (MH = MH) a repeated measures One-Way ANOVA was performed. For multiple comparisons between groups Tukey HSD test was used as the post Hoc. The significance level was subset at α = 0.05.


  Results Top


Seven specimens were lost during MH test and data of 98 specimens were subjected to statistical analysis. The means and standard deviations for MH of all groups are presented in [Table 1] and [Figure 1]. The maximum mean of MH was detected in Group 1 and then in Group 6; and Group 5 attained the minimum of MH.
Figure 1: The micro-hardness value of different groups of enamel preparation.

Click here to view
Table 1: The mean and standard deviation of micro-hardness in different groups of enamel preparation

Click here to view


The result of multiple comparisons is presented in [Table 2]. The comparison of Group 2 with Group 3 and Group 6 with Group 7 did not show considerable difference (P > 0.05). Furthermore, Group 2 did not show significant differences in comparison with Group 6 and 7. The other comparisons between groups revealed significant differences (P < 0.05).
Table 2: Two by two comparison of micro-hardness between the groups with different methods of enamel preparation

Click here to view



  Discussion Top


Etching enamel surface around the bonded brackets removes the fluoride-rich surface of the enamel and makes the enamel susceptible to demineralization during orthodontic treatment.[17] Artificial white spot formation on the enamel surface affects its MH.[18] So, we used MH test to evaluate the mineral loss that occurred among experimental groups. The results of this study indicate that any type of enamel conditioning decreases surface MH significantly, as it was suggested by previous studies.[19],[20],[21] Then, it is better not to condition the whole enamel surface for bonding the brackets.[10]

Conditioning with self-etch primers even two times, had minimum effect on MH. Applying self-etch primer only once showed the highest MH among the non-control groups. It has been shown that self-etch primers preserve the resistance of enamel to demineralization[22] and enamel conditioning with the conventional acid-etch method leads to more enamel loss than the self-etch primer technique.[23] Furthermore, Masahiro Iijima et al.[24] have shown that self-etch primers have the minimal effect on enamel hardness-evaluated by nanoindentor-and enamel elastic modulus compared to conventional bonding technique. These results are in agreement with the present study based on the higher MH in self-etch primer groups in comparison to conventional etch-rinse conditioning. Transbond self-etch primer does not affect enamel MH as much as the conventional etching technique. This bonding technique is based on preserving the hybrid layer which leads to more intact enamel surface. In groups which had two times of conditioning and primer bonding resembling the situation where bracket repositioning is needed in the same session of treatment, the cured primer was removed with polishing bur (G and H orthodontics, USA) each time. The polishing process affected those samples treated with the conventional method of enamel conditioning more than the self-etching primer method. This was stated by Ingrid Hosein et al.[23] that following enamel clean-up with different methods, conventional etching system causes more enamel loss in comparison to the self-etching system. Furthermore, it has been shown that self-etching primers cause less damage to the enamel in the secondary bonding process and have adequate bonding strength.[25]

After self-etch primer, etching the enamel without applying the primer had the least effect on MH. It seems that even two times of etching (each time for 15 s) made no differences in MH, although it has a nonsignificant declining trend. Therefore, if the clinician etches the enamel again in the re-bonding procedure, it will be better to restrict the area of primer application when using the conventional etch-and-rinse method.

Etching the enamel (once or twice) followed by primer application had the lowest MH values. Acid etch removes about 10–20 micrometers of the outer layer of enamel. Based on the result of the present study, it could be implied that when the enamel surface is etched and covered with the primer bonding agent, it would prevent the proper re-mineralization process. Our results showed that not only simple primers (Transbond XT) bonding did not have preventive effect on acid-etched enamel but even it might prevent the re-mineralization process of buffering cycle of saliva. This is also stated in a review article by Øgaard and Fjeld,[26] that etched enamel which was not covered by resin material undergoes re-mineralization relatively fast, following the salivary exposure. Although a study conducted by Yap et al.[27] declared that using resin-based sealant on enamel surface had physical protective effect around the bracket, this is implied only to sound enamel and it cannot be generalized to etched surfaces of the enamel. Furthermore, another study evaluated the effect of light-cured sealants on enamel demineralization and declared that unfilled sealants have no preventing effect.[28] The resin-based sealant may be protective in case of sound enamel surface by preventing micro-leakage in the surrounding margins of attachments. In the present study, repeating the conventional bonding procedure twice had the most effect on enamel hardness. On the other hand, it has been shown that etching the enamel is not necessary in the process of bracket re-bonding or repositioning.[29] Therefore, it can be suggested not to etch the enamel surfaces which have been etched and primed before.

Although this study tried to imitate the saliva buffering cycle (de-mineralization and re-mineralization), it did not include oral hygiene, fluoride supplements, and bacterial impact. Furthermore, in clinical conditions often there is a time interval between the initial bonding and the rebonding, and during this time the enamel might be remineralized. Therefore, it is suggested that these factors be considered in future studies. As a consequence, this study could not extrapolate the in-vivo situation completely.


  Conclusion Top


As the clinical relevance, it can be concluded that clinicians could affect the enamel MH during orthodontic treatments iatrogenically. Trying to prevent multiple surplus etchings or not to covering the etched surface of enamel that exceeds the bracket area can be beneficial. It is also recommended to use self-etching primers instead of conventional etching systems for more conservative treatments.

Acknowledgment

The authors would like to thank Dr. Mehrdad Vossoughi of the Dental Research Development Center of the School of Dentistry for the statistical analysis used in the study.

Financial support and sponsorship

Nil.

Conflicts of interest

The authors of this manuscript declare that they have no conflicts of interest, real or perceived, financial or nonfinancial in this article.



 
  References Top

1.
Buonocore MG. A simple method of increasing the adhesion of acrylic filling materials to enamel surfaces. J Dent Res 1955;34:849-53.  Back to cited text no. 1
    
2.
Chigira H, Koike T, Hasegawa T, Itoh K, Wakumoto S, Hayakawa T. Effect of the self etching dentin primers on the bonding efficacy of a dentin adhesive. Dent Mater J 1989;8:86-92.  Back to cited text no. 2
    
3.
Buyukyilmaz T, Usumez S, Karaman AI. Effect of self-etching primers on bond strength-are they reliable? Angle Orthod 2003;73:64-70.  Back to cited text no. 3
    
4.
Bishara SE, VonWald L, Laffoon JF, Warren JJ. The effect of repeated bonding on the shear bond strength of a composite resin orthodontic adhesive. Angle Orthod 2000;70:435-41.  Back to cited text no. 4
    
5.
Sadeq A, Risk JM, Pender N, Higham SM, Valappil SP. Evaluation of the co-existence of the red fluorescent plaque bacteria P. gingivalis with S. gordonii and S. mutans in white spot lesion formation during orthodontic treatment. Photodiagnosis Photodyn Ther 2015;12:232-7.  Back to cited text no. 5
    
6.
Demito CF, Vivaldi-Rodrigues G, Ramos AL, Bowman SJ. The efficacy of a fluoride varnish in reducing enamel demineralization adjacent to orthodontic brackets: An in vitro study. Orthod Craniofac Res 2004;7:205-10.  Back to cited text no. 6
    
7.
Khalaf K. Factors affecting the formation, severity and location of white spot lesions during orthodontic treatment with fixed appliances. J Oral Maxillofac Res 2014;5:e4.  Back to cited text no. 7
    
8.
Featherstone JD. The science and practice of caries prevention. J Am Dent Assoc 2000;131:887-99.  Back to cited text no. 8
    
9.
Kuhar M, Cevc P, Schara M, Funduk N. Enhanced permeability of acid-etched or ground dental enamel. J Prosthet Dent 1997;77:578-82.  Back to cited text no. 9
    
10.
Knösel M, Bojes M, Jung K, Ziebolz D. Increased susceptibility for white spot lesions by surplus orthodontic etching exceeding bracket base area. Am J Orthod Dentofacial Orthop 2012;141:574-82.  Back to cited text no. 10
    
11.
Cehreli ZC, Altay N. Effects of a nonrinse conditioner and 17% ethylenediaminetetraacetic acid on the etch pattern of intact human permanent enamel. Angle Orthod 2000;70:22-7.  Back to cited text no. 11
    
12.
Vicente A, Bravo LA, Romero M. Influence of a nonrinse conditioner on the bond strength of brackets bonded with a resin adhesive system. Angle Orthod 2005;75:400-5.  Back to cited text no. 12
    
13.
Graber LW, Vanarsdall RL, Vig KW, Huang GJ. Orthodontics-E-Book: Current Principles and Techniques. Amsterdam: Elsevier Health Sciences; 2016.  Back to cited text no. 13
    
14.
O'Reilly MM, Featherstone JD. Demineralization and remineralization around orthodontic appliances: An in vivo study. Am J Orthod Dentofacial Orthop 1987;92:33-40.  Back to cited text no. 14
    
15.
Argenta RM, Tabchoury CP, Cury JA. A modified pH-cycling model to evaluate fluoride effect on enamel demineralization. Pesqui Odontol Bras 2003;17:241-6.  Back to cited text no. 15
    
16.
Sakaguchi RL, Powers JM. Craig's restorative dental materials-e-book. Amsterdam: Elsevier Health Sciences; 2012 Jul 16.  Back to cited text no. 16
    
17.
Legler LR, Retief DH, Bradley EL. Effects of phosphoric acid concentration and etch duration on enamel depth of etch: An in vitro study. Am J Orthod Dentofacial Orthop 1990;98:154-60.  Back to cited text no. 17
    
18.
Arends J, Schuthof J, Jongebloed WG. Lesion depth and microhardness indentations on artificial white spot lesions. Caries Res 1980;14:190-5.  Back to cited text no. 18
    
19.
Kohda N, Iijima M, Brantley W, Muguruma T, Yuasa T, Nakagaki S, et al. Effects of bonding materials on the mechanical properties of enamel around orthodontic brackets. Angle Orthod 2012;82:187-95.  Back to cited text no. 19
    
20.
Davidson CL, Hoekstra IS, Arends J. Microhardness of sound, decalcified and etched tooth enamel related to the calcium content. Caries Res 1974;8:135-44.  Back to cited text no. 20
    
21.
Poole M. Efficacy of Orthodontic Bonding Agents in Preventing Demineralization Around Brackets. Virginia commonwealth university; 2010.  Back to cited text no. 21
    
22.
Montasser MA, El-Wassefy NA, Taha M. In vitro study of the potential protection of sound enamel against demineralization. Prog Orthod 2015;16:12.  Back to cited text no. 22
    
23.
Hosein I, Sherriff M, Ireland AJ. Enamel loss during bonding, debonding, and cleanup with use of a self-etching primer. Am J Orthod Dentofacial Orthop 2004;126:717-24.  Back to cited text no. 23
    
24.
Iijima M, Muguruma T, Brantley WA, Ito S, Yuasa T, Saito T, et al. Effect of bracket bonding on nanomechanical properties of enamel. Am J Orthod Dentofacial Orthop 2010;138:735-40.  Back to cited text no. 24
    
25.
Khosravani Fard B, Fetrati A, Asadi E. Comparison between self-etching and conventional primers in repeated bracket bonding. J Res Dent Maxillofac Sci 2017;2:20-32.  Back to cited text no. 25
    
26.
Øgaard, Bjørn, and Morten Fjeld. The enamel surface and bonding in orthodontics. Seminars in orthodontics, 2010; 16: 37-48  Back to cited text no. 26
    
27.
Yap J, Walsh LJ, Naser-Ud Din S, Ngo H, Manton DJ. Evaluation of a novel approach in the prevention of white spot lesions around orthodontic brackets. Aust Dent J 2014;59:70-80.  Back to cited text no. 27
    
28.
Hu W, Featherstone JD. Prevention of enamel demineralization: An in-vitro study using light-cured filled sealant. Am J Orthod Dentofacial Orthop 2005;128:592-600.  Back to cited text no. 28
    
29.
Nicolás AI, Vicente A, Bravo LA. The in vitro effect of repeated bonding on the shear bond strength with different enamel conditioning procedures. Eur J Orthod 2010;32:291-6.  Back to cited text no. 29
    


    Figures

  [Figure 1]
 
 
    Tables

  [Table 1], [Table 2]



 

Top
 
 
Search
Similar in PUBMED
   Search Pubmed for
   Search in Google Scholar for
 Related articles
Access Statistics
Email Alert *
Add to My List *
* Registration required (free)  

 
  In this article
Abstract
Introduction
Materials and Me...
Results
Discussion
Conclusion
References
Article Figures
Article Tables

 Article Access Statistics
    Viewed260    
    Printed8    
    Emailed0    
    PDF Downloaded46    
    Comments [Add]    

Recommend this journal